About the Products
MDF FR (FLAME RETARDANT MDF)
MDF FR is a low-ignition MDF with a red core layer. It is suitable for melamine coating and can be used as a core material for fire-resistant laminates. With its low ignition value and smooth, homogeneous surface, it is suitable for all kinds of decorative surface coatings.
Flame-retardant materials are colored with a red pigment to distinguish them from other products.
Application Areas
It is used in furniture and interior decoration, wall and ceiling cladding, partition walls, doors, flooring, exhibition stands, hotel interiors, offices, public institutions (libraries, schools, etc.), hospital furniture, and cinema furniture.
Çamsan Ordu FR MDF Technical Specifications Table GENERAL FEATURES TEST METHOD UNIT =6 >6 >8 >8>10 >10>14 >14>16 >16>19 FIGRA0.2MJ EN ISO 13823 (W/s) A2: <120 Ws
B: <120 WsFIGRA0.4MJ THR600s (MJ) A2: < 7,5 MJ, B: < 7,5 MJ SMOGRA (m²/s²) S1: < 30 m²/s², S2: < 180 m²/s² TSP600s (m²) (m²) S1: < 50 m²/s², S2: < 200 m²/s² FDP S d0: Kein Brennen / no flaming, d1: < 10s Burning Duration / Flaming, d2: > 10s Burning Duration / Flaming LFS Yes / No LFS < Edge of Specimen (Yes - No) Fs Exposure = 30s EN ISO 11925-2 S FS ≤ 150 mm within 60 s Flaming droplets (Yes - No) Thickness Tolerance EN 324-1 mm ±0,3 mm Width and Length Tolerance EN 324-1 mm/m ± 2,0 max. ±5,0 mm Perpendicularity Tolerance EN 324-2 mm/m ± 2,0 Density EN 323 kg/m³ 815 815 800 790 Density Tolerance EN 323 % ± 5 Moisture Content EN 323 % 4 - 11 Formaldehyde Emission EN 120 mg/100 g E1 ≤ 8,0 mg / 8,0 < E2 ≤ 30,0 mg ASTM D-6007 ppm CARB 0,11 - 0,13 ppm EN 717-1 mg/m³ E 0,5 0,062 mg/m³ Tensile Strength EN 319 N/mm² 0,65 0,6 0,55 Flexural Strength EN 310 N/mm² 2700 2500 2200 Swelling (24 Hours) EN 310 N/mm² ≤30 ≤17 ≤15 ≤12 Elastic Modulus EN 317 % 23 22 20 Surface Porosity EN 382-1 mm 150
Çamsan Ordu FR MDF Test Results Table TEST METHOD GENERAL PROPERTIES UNIT TECHNICAL SPECIFICATIONS 6 – 18 mm EN ISO13823 FIGRA0.2MJ (W/s) A2: < 120 Ws
B: < 120 Ws60 – 76,4 FIGRA0,4 MJ THR600s (MJ) A2: < 7,5 MJ
B: < 7,5 MJ2,5 – 6,5 SMOGRA (m²/s²) S1: ≤ 30 m²/s²
S2: ≤ 180 m²/s²2 – 8,0 TSP600s (m²) S1: ≤ 50 m²/s²
S2: ≤ 200 m²/s²43 – 97,9 FDP S d0: No Burning / No Flame
d1: < 10 s Burning Time / Flaming
d2: > 10s Burning Time / Flamingd0 EN ISO13823 LFS Yes / No LFS < Edge of specimen (Yes - No) CONFORMS EN ISO 11925-2 Fs
Exposure =
30 sS FS ≤ 150 mm within 60 s 60 s Flaming Droplets (Yes - No) CONFORMS
Burning Behavior / Reaction to Fire Smoke Production Flaming droplets/particles B S 2 D 0
Reaction to Fire Classification: B-s2,d0
FIGRA0.2MJ : Fire growth value [W/s] after calibration of the 0.2 MJ THR threshold; Fire Growth Rate [W/s] after reaching a THR threshold of 0.2 MJ.
FIGRA0,4 MJ : Fire growth value [W/s] after calibration of the 0.4 MJ THR threshold; Fire Growth Rate [W/s] after the 0.4 MJ THR limit is reached.
THR600s : Total heat released during the first 600 seconds of flame contact [MJ], Total heat released during the first 600 seconds of flame contact [MJ]
SMOGRA : Smoke generation rate [m²/s²], Smoke Growth Rate [m/s]; s1: Low smoke production, s2: Moderate smoke production, s3: High smoke-producing materials.
TSP600s : Total amount of smoke released during the first 600 seconds of flame contact [m²], total smoke production resulting from the first 600 seconds of flame contact [m]
LFS: The lateral flame spread toward the outer edge of the long specimen wing. The lateral spread of the flame reached the farthest edge of the large specimen wing.
FDP : Burning and dripping occurred within the first 600 seconds of exposure; flaming droplets/particles [s] during the first 600 seconds of the flame.
Fs: Vertical flame spread distance on the test specimen surface, Flaming Droplets. Flame spread [mm]